Stainless Steel 410S Grade Sheet plates .
Metal Scope (INDIA)
General Properties
Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410S (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden. 410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410Sis completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410S and good oxidation resistance.
Corrosion Resistance
The corrosion resistance of Sandmeyer Steel 410Sstainless steel is similar to type 410S. It resists corrosion in atmospheric conditions, fresh water, mild organic and mineral acids, alkalis and some chemicals. It’s exposure to chlorides in everyday activities (e.g., food preparation, sports activities, etc.) is generally satisfactory when proper cleaning is performed after exposure to use.
The oxidation resistance of 410S stainless steel is good. It can be used in continuous service up to 1300°F (705°C). Scaling becomes excessive above 1500°F (811°C) in intermittent service
Fabrication Data
Heat Treatment
The alloy can not be hardened by heat treatment. It is annealed in the 1600 – 1650°F (871 – 899°C) range and then air cooled to relieve cold working stresses. 410S should not be exposed to temperatures of 2000°F (1093°C) or above due to embrittlement. If excessive large grains are encountered after annealing mildly cold-worked material, the annealing temperature should be decreased to a range of 1200 – 1350°F (649 – 732°C) range.
Surface Preparation
For maximum corrosion resistance to chemical environments, it is essential that the 410S surface be free of all heat tint or oxide formed during annealing or hot working. All surfaces must be ground or polished to remove any traces of oxide and surface decarburization. The parts should then be immersed in a warm solution of 10-20% nitric acid followed by a water rinse to remove any residual iron.
Machining
Alloy 410S should be machined in the annealed condition using surface speeds of 60 to 80 feet (18.3 – 24.4 m) per minute.
Alloy 410S stainless steel is a low carbon modification of Type 410S stainless steel. Low carbon and optionally a small addition of titanium and/ or columbium minimize austenite formation at high temperatures, thereby restricting the alloy's ability to harden. The material remains soft and ductile even when the material is rapidly cooled from above the critical temperature. This low hardening characteristic helps to prevent cracking when the steel is welded or exposed to high temperatures. The alloy is completely ferritic in the annealed condition. 410S is ferromagnetic.@metalscope.in
Welding
For maximum corrosion resistance to chemical environments, it is essential that the 410S surface be free of all heat tint or oxide formed during annealing or hot working. All surfaces must be ground or polished to remove any traces of oxide and surface decarburization. The parts should then be410S\ is generally considered to be weldable by the common fusion and resistance techniques. Special consideration should be given to avoid brittle weld fractures during fabrication by minimizing discontinuities, maintaining low weld heat input and occasionally warming the part somewhat before forming. 410S is generally considered to have slightly poorer weldability than the most common ferritic stainless steel grade 409. A major difference can be attributed to the alloy addition to control hardening which results in the need for higher heat input to achieve penetration during arc welding. When a weld filler is required, AWS E/ER 309L or 430 filler material is most often specified.immersed in a warm solution of 10-20% nitric acid followed by a water rinse to remove any residual iron.
CHEMICAL COMPOSITION:
Element |
Type 410S |
Carbon |
0.08 max. |
Manganese |
1.00 max. |
Sulfur |
0.030 max. |
Phosphorus |
0.040 max. |
Silicon |
1.00 max. |
Chromium |
11.5 – 13.5 |
Nickel |
0.60 max. |
MECHANICAL PROPERTIES: ASTM A240
Type |
Yield Strength |
UTS |
% EL |
Hardness |
410S |
205 min. |
415 min. |
22 min. |
89 HRB MAX |
Type 410S is a low carbon, non-hardening version of Type 410S stainless steel. This general-purpose stainless steel remains soft and ductile even when rapidly cooled. Other key benefits of Type 410S include:
- Weldable by most common techniques
- Good resistance to oxidation
- Continuous services up to 1300°F (705°C)
- Similar corrosion resistance to Type 410S, good in fresh water and mild organic and mineral acids
Because of its unique properties and chemical composition, Type 410S is useful for a variety of applications in a large range of critical industries including:
- Petroleum refining
- Petrochemical processing
- Thermal processing
- Gate valves
- Press plates
- Heat exchangers
- Ore processing and mining machinery
Continental Steel supplies Type 410S stainless steel in a number of different forms and sizes all of which meet some of the toughest international standards including, ASTM A 240 and ASME SA 240.
ASTM A182/ ASME SA182 Stainlees Steel Pipe Fittings • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Plates • ASTM A213 / ASME SA213 Seamless Stainless Steel Plates • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Plates • ASTM A240/ ASME SA240 Stainless Steels Sheets / Plates • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Round Bar • ASTM A249/ ASME SA249 Stainless Steel Sheets • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Tube • ASTM A269/ ASME SA269 Stainless Steel Sheets • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Flanges • ASTM A270/ ASME SA270 Stainless Steel Sanitary Sheets • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Wire • ASTM A312/ ASME SA312 Stainless Steel Plates • SS 410S, Type 410S, WNR 1.4000, UNS S41008, AISI 410S Fittings • ASTM A403/ ASME SA403 Stainless Steel Pipe Fittings • ASTM A554/ ASME SA554 Stainless Steel Welded Sheets • ASTM A731/ ASME SA731 Stainless Steel Plates • ASTM A789/ ASME SA789 Stainless Steel Sheets • ASTM A790/ ASME SA790 Stainless Steel Plates • ASTM A791/ ASME SA791 Stainless Steel Sheets
Metal Scope (INDIA) continues to expand its product line in UNS S41008 to meet the emerging customer needs, and whereas. is ISO 9001 : 2008 Certified has a great Projects in this grade in all parts of the world with renowned suppliers presenting the wide range of services. We pride ourselves in the quality of our products, our competitive pricing and our exceptional customer service. We have been recognized for our outstanding customer service in satisfaction surveys of top- ranked mills in india and all over the world. the right time and the right time and the right area. We strive and stand commited to maintain this respectable position by catering to the requirements of our customers in the best possible way leaving no room for complaints. www.metalscope.in
410S Stainless Steel
410S - UNS S41008:
AISI Type 410S is a non-hardenable, low carbon modification of Type 410S, providing moderate strength with moderate corrosion resistance. The low carbon content and a small titanium addition minimizes austenite formation at high temperatures, thereby restricting the alloy's ability to harden. The result is a soft, ductile condition when the material is rapidly cooled from above the critical temperature. The alloy is completely ferritic. Thermal conductivity is improved and thermal expansion reduced relative to austentic stainless grades. www.metalscope.in
Similar performing non-hardenable grades include UNS S41003 and UNS S40920 (AISI Type 409)
Corrosion Resistance:
The corrosion resistance of 410S Stainless Steel is similar to Type 410S. It provides adequate resistance to atmospheric corrosion, fresh water, mild acids and alkalis, and some other chemicals.
Specifications
ASTM A 240, ASTM SA 240, EN 1.4000, UNS S41008, Werkstoff 1.4000
Stainless Steel 410S Plates |
SS 410S plates |
Stainless Steel 410S Plates |
SS 410S ASTM A240 Plates Exporter |
Stainless Steel 410SChequered Plate |
ASTM A240 SS 410S Plates Supplier |
DIN X12Cr13 SS Diamond Chequered Plate |
410S SS Plates Manufacturers |
UNS S410S00 SS Plate Stockholder |
Cold Rolled Stainless Steel 410S Plates |
Stainless Steel 410S Plate 2B Finish Dealer |
#4 Finish Stainless Steel 410S Plates |
Cut to Size Stainless Steel 410S Plates |
Hot Rolled Stainless Steel 410S Plates |
Stainless Steel 410S CR Plates Stockist |
Stainless Steel 410S HR Plates Dealer |
Leading Manufacturer Of Stainless Steel 410S Plates |
ASTM A240 High Quality SS 410S Plates, |
ASME SA 240 SS 410S Plates Distributors SS 410S Grade Sheets / plates Supplier UNS S410S Grade Sheets / plates Supplier UNS S410SGrade coils distributor |
410S Stainless Steel Plates Exporter SS 410S Grade Coils Supplier UNS S410SGrade coils Supplier |
Stainless Steel 410S Polished Plates, SS 410S Polished Plates, 410S SS Polished Plates, 410S Stainless Steel Polished Plates, Stainless Steel 410S Hot Rolled Plates, SS 410S Hot Rolled Plates, 410S SS Hot Rolled Plates, 410S Stainless Steel Hot Rolled Plates, Stainless Steel 410S Cold Rolled Plates, SS 410S Cold Rolled Plates, 410S SS Cold Rolled Plates, 410S Stainless Steel Cold Rolled Plates, Stainless Steel 410S Coils, SS 410S Coils, 410S SS Coils, 410S Stainless Steel Coils, Stainless Steel 410S Strips, SS 410S Strips, 410S SS Strips, 410S Stainless Steel Strips, Stainless Steel 410S Foils, SS 410S Foils, 410S SS Foils, 410S Stainless Steel Foils, Stainless Steel 410S Shim Sheet . Metalscope.in